Heat shrink tubing for terminals and crimp splice
2024/7/24 viewers259
- BrandDEEM
- TypeDM-TCS
Introduction
ApplicationsManufactured by co-extrusion polyolefin and polyamide, it has excellent tensile strength,
puncture resistance and waterproof properties. Specially designed for environment sealing
and protection of crimp splices and terminations.
Features
Shrink ratio: 3:1
Excellent puncture resistance
High peel strength.
Abrasion and corrosion resistance.
Waterproof and moisture resistance.
Various
Operating temperature: - 55°C to +125°C
Minimum shrink temperature: 80°C
Minimum fully recovery temperature: 130°C
Standard color: Red, blue, yellow
Technical Data
| Property | Test Method | Values |
| Tensile strength | Room temp | ≥16 MPa |
| Elongation at break | ≥200% | |
| Voltage withstand and breakdown Voltage | Withstand 2.5KV for 1minute and breakdown | |
| Tensile strength at aging | 158℃/7days | ≥11.5 MPa |
| Elongation at break at aging | ≥100% | |
| Voltage withstand and breakdown Voltage at aging | At least half of un-aged breakdown voltage | |
| Copper corrosion | No sign of degradation | |
| Copper stability | No drop, no flow | |
| Cold bend | -30℃/4 hrs | No cracking |
| Maximum secant modulus (2%) | 250MPa | |
| Volume resistivity | Min.1014 Ω·cm | |
| Heat shock | 250°C/4 hrs | No cracking |
| As Supplied (mm) | After Recovery (mm) | Standard length | ||
|
Inside Diameter
Min. (D)
|
Wall Thickness
Min. (WT)
|
Inside Diameter
Min. (D)
|
Wall Thickness
Min. (WT)
|
m/roll |
| Φ3.2±0.3 | 0.35±0.05 | Φ1.0 | 1.0±0.1 | 100 |
| Φ4.8±0.3 | 0.45±0.05 | Φ1.4 | 1.1±0.1 | 100 |
| Φ7.0±0.3 | 0.45±0.05 | Φ2.5 | 1.2±0.1 | 100 |
| Φ6.8±0.3 | 0.5±0.05 | Φ3.0 | 1.4±0.1 | 100 |
| Φ7.0±0.3 | 0.5±0.05 | Φ2.5 | 1.5±0.1 | 100 |
| Φ8.3±0.3 | 0.65±0.05 | Φ3.0 | 1.65±0.1 | 100 |